Description:

Thermosetting powder coating based on a blend of epoxy and polyester. Hybrids are designed for interior applications where exterior durability is not required. This product contains aluminum. If the product is to be cleaned, handled consistently or is in an abrasive environment it is recommended that it should be top coated with a clear coat.

Typical Applications:

Decorative finishes

Typical Properties:

Film Thickness
Gloss 60'angle (ASTM D-523-89)
Hardness (ASTM D-3363-92A)
Flexibility (ASTM D-1737-89)
Adhesion (ASTM D-3359-95A)
Impact Direct/Indirect (ASTM D-2794-93)
Exterior Durability
Chemical Resistance
Salt Spray (ASTM B117)
Specific Gravity (calculated)

2.5 – 4.0+ mil
Semi
2H
1/8 inch
5b (100%)
up to 160 in-lbs
Poor
Good – Very Good
1000Hrs < 1/8”
1.5

Application Data:

Hybrids are to be applied with a corona electrostatic powder spray gun at between 60kv – 100 kv. Hybrids can also be formulated for tribo or fluid bed application upon request.

Cure Schedule:

Hybrids can be cured in a direct or indirect gas convection oven, an electric oven, or an Infra red. A combination of any of these ovens is also suitable.
Standard Cure:     10 Minutes @ 375⁰f Peak Metal Temperature

Storage:

Product should be stored at temperatures below 80⁰f, in a dry area away from any heat source

Notes:

All tests were performed on Bonderite 1000, iron phosphated panels with a nominal film thickness of 2 mils.
Lower gloss levels may require higher cure temperatures or longer dwell times.
Please refer to the MSDS for safety information.